M. v. Sivers, C. Ciemniak, A. Erb, F. v. Feilitzsch, A. Gütlein, J. -C. Lanfranchi, J. Lepelmeier, A. Münster, W. Potzel, S. Roth, R. Strauss, U. Thalhammer, S. Wawoczny, M. Willers, A. Zöller
We investigate the influence of oxygen annealing on the room temperature optical and scintillation properties of CaWO$_4$ single crystals that are being produced for direct Dark Matter search experiments. The applied annealing procedure reduces the absorption coefficient at the peak position of the scintillation spectrum ($\sim430$ nm) by a factor of $\sim6$ and leads to an even larger reduction of the scattering coefficient. Furthermore, the annealing has no significant influence on the \emph{intrinsic} light yield. An additional absorption occurring at $\sim400$ nm suggests the formation of O$^-$ hole centers. Light-yield measurements at room temperature where one crystal surface was mechanically roughened showed an increase of the \emph{measured} light yield by $\sim40 %$ and an improvement of the energy resolution at 59.5 keV by $\sim12 %$ for the annealed crystal. We ascribe this result to the reduction of the absorption coefficient while the surface roughening is needed to compensate for the also observed reduction of the scattering coefficient after annealing.
View original:
http://arxiv.org/abs/1206.1588
No comments:
Post a Comment